What is the effect of low pouring temperature on casting quality?Blow HolesCold shutsMiss Runs

The effect of low pouring temperature on casting quality can result in several issues such as blow holes, cold shuts, and miss runs. Let's break down each of these effects step by step:

1. Blow Holes: When the pouring temperature is too low, it can lead to the formation of blow holes in the casting. Blow holes are cavities or voids that form due to the entrapment of gases during the solidification process. These blow holes can weaken the casting and reduce its overall integrity.

2. Cold Shuts: Another effect of low pouring temperature is the occurrence of cold shuts. Cold shuts are defects that happen when the molten metal does not properly fuse together during solidification. This can result in a weak joint or seam in the casting, compromising its structural integrity.

3. Miss Runs: Low pouring temperature can also lead to miss runs in the casting. Miss runs occur when the molten metal does not completely fill the mold cavity, resulting in incomplete or distorted castings. This can lead to dimensional inaccuracies and defects in the final product.

In summary, low pouring temperature can have detrimental effects on casting quality, including the formation of blow holes, cold shuts, and miss runs. It is important to carefully control the pouring temperature to ensure proper solidification and minimize these defects.